Influence of microstructure changes on corrosion resistance of super duplex stainless steel Online publication date: Sun, 04-Apr-2010
by A.M. Elhoud, N.C. Renton, D.A. Lasebikan, W.F. Deans
International Journal of Microstructure and Materials Properties (IJMMP), Vol. 5, No. 1, 2010
Abstract: Effect of microstructure on pitting corrosion of super duplex was investigated in 3.5% NaCl solution at 90°C. The microstructures were controlled by applying two different cooling rates of water quench and air from the heat treatment temperatures of 1,000°C and 1,300°C. The amount of ferrite and austenite and other precipitates were measured using optical and image analyser. The results revealed that the ferrite percentage increased as the heating temperature increased to 1300°C. Metallographic results showed the presence of intermetallic phases. Back scattering analysis revealed presence of sigma (σ) and chi (χ) phase. The volume fraction of ferrite to austenite as well as the precipitation of harmful intermetallic phase during cooling process affected the corrosion resistance. Reformation of austenite during slow cooling from 1,300°C enhanced corrosion resistance while intermetallic precipitates promoted pitting damage and decreased pitting potential to more active values.
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Microstructure and Materials Properties (IJMMP):
Login with your Inderscience username and password:
Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.
If you still need assistance, please email subs@inderscience.com