Surface modification of carbonised waste rice husks by mild hydrothermal treatment Online publication date: Mon, 19-Apr-2021
by Wong Min Jin Karen; J.X. Ooi; Zhipeng Wang; Nancy J. Siambun; Willey Y.H. Liew; W.K. Muzammil; K. Sopian; G.J.H. Melvin
International Journal of Surface Science and Engineering (IJSURFSE), Vol. 15, No. 1, 2021
Abstract: Carbonisation process is a way in exploiting rice husk to produce alternative carbon material. In this study, rice husk was carbonised at 500°C, 2 h in inert environment. Mild hydrothermal treatment of carbonised rice husk was conducted by using potassium hydroxide (KOH) and potassium persulfate (KPS) as reactants in different parameters: 1) the reactants molar ratio; 2) reaction time. The treated carbonised rice husks were tested for its dispersion, morphology observation, elements and functional groups determination. From the results, the modified carbonised rice husks showed improvement in its dispersion with polar solvent while no defects in the structures were observed from the SEM images. High oxygen content was found in EDX analysis for modified carbonised rice husks treated in KOH: KPS with molar ratio of 3:1. The presence of hydroxyl and carboxyl groups from the FTIR spectra shows that the treatment successfully introduced functional group to the carbonised rice husk surface.
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Surface Science and Engineering (IJSURFSE):
Login with your Inderscience username and password:
Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.
If you still need assistance, please email subs@inderscience.com