Falling weight impact damage characterisation on flax/epoxy laminates Online publication date: Wed, 12-Aug-2009
by Carlo Santulli
International Journal of Materials and Product Technology (IJMPT), Vol. 36, No. 1/2/3/4, 2009
Abstract: Unidirectional flax/epoxy laminates manufactured using different threads (0.2, 0.9 and 2.3 mm diameter) of untreated flax fibres were tested statically and dynamically (falling weight impact) in a three-point flexural rig. Despite the lower amount of fibres introduced (31% wt. against 55% wt. for both the other laminates), the laminates manufactured using the finest thread did not show lower mechanical properties. This outcome was explained by improved resin impregnation and consequent lower void content, resulting in lower spalling (material loss at rear). Also the study of impact hysteresis curves clarified that a comparable penetration energy is absorbed from the three laminates.
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Materials and Product Technology (IJMPT):
Login with your Inderscience username and password:
Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.
If you still need assistance, please email subs@inderscience.com