Influences of welding processes on microstructure and mechanical properties of modified 12 wt % Cr ferritic stainless steel Online publication date: Sat, 22-Nov-2014
by A.K. Lakshminarayanan; V. Balasubramanian
International Journal of Manufacturing Research (IJMR), Vol. 7, No. 4, 2012
Abstract: This paper presents the comparative evaluation of microstructural features and mechanical properties of a friction stir welded (solid-state), gas tungsten arc welded (fusion), electron beam and laser beam welded (high energy density) 409M grade ferritic stainless steel joints. Optical microscopy, ferritescope measurements, X-ray diffraction analysis, microhardness, transverse tensile, impact and bend tests were performed. The coarser ferrite grains in the base material are changed to very fine grains consisting duplex structure of ferrite and martensite due to the rapid cooling rate and high strain induced by severe plastic deformation caused by frictional stirring. Fine dendritic columnar grain structure of alpha ferrite with grain boundary martensite was observed in fusion zone of laser and electron beam welded joints. On the other hand, grain growth was observed in fusion zone as well as high temperature heat affected zone of gas tungsten arc welded joint resulting in deterioration of mechanical properties. [Received 17 September 2010; Revised 13 December 2010; Accepted 27 June 2011]
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Manufacturing Research (IJMR):
Login with your Inderscience username and password:
Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.
If you still need assistance, please email subs@inderscience.com