Optimisation of wear behaviour of heat treated Ti-6Al-4V alloy by response surface methodology Online publication date: Sun, 09-Jul-2017
by S. Thirumalvalavan; P. Malliga
International Journal of Materials and Product Technology (IJMPT), Vol. 55, No. 1/2/3, 2017
Abstract: Titanium alloys are extensively used in various fields of engineering, medicine, aerospace and marine due to their excellent mechanical properties. The response of the Ti alloys for its wear resistance is very poor. In this research the wear behaviour of the Ti alloys is improved by the heat treatment process. In this research, the implant material is subjected to heat treatment above its transformation temperature (950°C) followed by cooling in furnace. These specimens were further aged at 550°C for three hours and then water quenched. The property of poor wear resistance can be improved by changing the microstructure of the alloy where the formation martensitic structure (acicular α or retained β) is resulted. The wear test was conducted using the pin-on-disk, with varying parameters of the applied load (10-50 N), speed (100-500 rpm) and time (5-25 min). Scanning electron micrographs (SEM) exhibit the wear scars and worn surfaces of the tested specimens. The optimum parameters were optimised by the response surface methodology and some useful conclusions were made.
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Materials and Product Technology (IJMPT):
Login with your Inderscience username and password:
Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.
If you still need assistance, please email subs@inderscience.com